Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | | 0.60 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 7.00 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 0.30-0.70 % |
| Water absorption rate | | ISO 62 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 84 |
| ball-indentation hardness | | ISO 2039-1 | 175 Mpa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ISO 489 | 1.567 |
| transmissivity | | ASTM D1003 | >89.0 % |
| Haze ratio | | ASTM D1003 | <1.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3900 Mpa |
| tensile strength | | ISO 527-2 | 79.0 Mpa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| bending strength | | ISO 178 | 135 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 21 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 20 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| dielectric constant | | IEC 60250 | 3.00 |
| Dissipation Factor | | IEC 60250 | 5E-03 |
| Dissipation Factor | | IEC 60250 | 7E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 110 °C |
| Heat distortion temperature | | ISO 75-2/A | 104 °C |
| vicat | | ISO 306/B50 | 120 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
| thermal conductivity | | DIN 52612 | 0.17 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.