Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.35 -- |
| Shrinkage rate | | % | 0.50 -- |
| Shrinkage rate | | % | 0.10 -- |
| Water absorption rate | | % | 6.7 -- |
| Water absorption rate | | % | 2.3 -- |
| viscosity number | | cm³/g | 150 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | % | 2.7 6.5 |
| Tensile modulus | | MPa | 6400 3500 |
| tensile strength | Yield | MPa | 150 100 |
| tensile strength | Break | MPa | 110 50.0 |
| Tensile strain | Yield | % | 3.0 5.5 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 5.0 5.0 |
| Charpy Notched Impact Strength | | kJ/m² | 7.0 13 |
| Impact strength of simply supported beam without notch | | kJ/m² | 40 40 |
| Impact strength of simply supported beam without notch | | kJ/m² | 45 55 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+12 -- |
| dielectric strength | | kV/mm | 31 -- |
| | | 3.90 -- |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 1 |
| Surface Resistivity | | ohms | 1E+10 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | °C | 215 -- |
| Hot deformation temperature (HDT) | | °C | 200 -- |
| melting temperature | | °C | 222 -- |
| | cm/cm/°C | 6.0E-5到1.1E-4 -- |
| | cm/cm/°C | 3.4E-5到3.8E-5 -- |
| Hot deformation temperature (HDT) | | °C | <350 <350 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.