PP Homopolymer MOSTEN MB 720
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 18 g/10min | |
| Shrinkage rate | ISO 294-4 | 2.2 % | |
| ISO 294-4 | 2.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 60 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 1100 MPa | |
| tensile strength | Yield | ISO 527-2 | 21.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 5.0 % |
| Break | ISO 527-2 | 100 % | |
| Tensile creep modulus | ISO 899-1 | 760 MPa | |
| ISO 899-1 | 300 MPa | ||
| Flexural modulus | ISO 178 | 1050 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1 | 7.0 kJ/m² | |
| ISO 179/1 | 45 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 52.0 °C | |
| vicat | ISO 306 | 145 °C | |
| melting temperature | ISO 11357-3 | 165to170 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.