PC XANTAR® 27 R Mitsubishi Chemical Corporation

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity		ASTM D1003	89.0 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/4A	80 kJ/m²

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ISO 4589-2	26 %
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875 °C
Hot filament ignition temperature	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	825 °C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	V-2
UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	V-2
Burning wire flammability index	1.5mm	IEC 60695-2-12	800 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	90.0 MPa
Bending modulus		ISO 178	2400 MPa
Nominal tensile fracture strain		ISO 527-2	>50 %
Tensile strain	Yield	ISO 527-2	6.0 %
tensile strength	Yield	ISO 527-2	60.0 MPa
Tensile modulus		ISO 527-2	2300 MPa

thermal performance	Test Condition	Test Method	Test Result
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Vicat softening temperature		ISO 306/B50	150 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	130 °C
RTI Str	3.0mm	UL 746	130 °C
RTI Str	RTI Str	1.5mm	UL 746	125 °C
RTI Imp	3.0mm	UL 746	130 °C
RTI Imp	RTI Imp	1.5mm	UL 746	125 °C
RTI Elec	3.0mm	UL 746	130 °C
RTI Elec	RTI Elec	1.5mm	UL 746	130 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
ThermalConductivityofMelt			0.24 W/m/K
density		ISO 1183	1.20 g/cm³
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	3.00 cm³/10min
Shrinkage rate	MD	ISO 294-4	0.60 %
Water absorption rate	Saturation,23°C	ISO 62	0.35 %
LimitingViscosity		ISO 1628-4	61.0 cm³/g

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	>1.0E+15 ohms
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	PLC 3
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dielectric strength		IEC 60243-1	29 kV/mm
Relative permittivity	100Hz	IEC 60250	3.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	2.90
Dissipation factor	100Hz	IEC 60250	6.6E-04
Dissipation factor	Dissipation factor	1MHz	IEC 60250	9.2E-03

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ISO 2039-2	70

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.