Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.70 g/cm³ |
| Melt volume flow rate | | ISO1133 | 14.0 cm3/10min |
| Shrinkage rate | | ISO2577 | 0.82 % |
| Shrinkage rate | | ISO294-4 | 0.12 % |
| Shrinkage rate | | ISO2577 | 0.16 % |
| Shrinkage rate | | ISO2577 | 0.030 % |
| Water absorption rate | | ISO62 | 7.0 % |
| Water absorption rate | | ISO62 | 2.1 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 210 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 600 °C |
| Extreme Oxygen Index 11 | | ISO4589-2 | 22 % |
| BurningBehavior12 | | ISO3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO1874 | PA6,GR,14-100,GF30 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 80 kJ/m² |
| | ISO180/1U | 60 kJ/m² |
| | ISO180/1U | 75 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus 4 | | ASTMD638 | 9200 Mpa |
| Tensile modulus | | ISO527-2/1 | 9800 Mpa |
| tensile strength | | ASTMD638 | 180 Mpa |
| Tensile stress | | ISO527-2/5 | 180 Mpa |
| elongation | | ASTMD638 | 3.0 % |
| Tensile strain | | ISO527-2/5 | 3.0 % |
| TensileCreepModule | | ISO899-1 | -- Mpa |
| Tensile creep modulus | | ISO899-1 | -- Mpa |
| Flexural modulus | | ASTMD790 | 8270 Mpa |
| Flexural modulus | | ISO178/A | 8600 Mpa |
| bending strength | | ASTMD790 | 280 Mpa |
| Bending stress 5 | | ISO178/A | -- Mpa |
| Bending stress 5 | | ISO178 | 280 Mpa |
| Bending stress 5 | | | 4.0 % |
| film | Test Condition | Test Method | Test Result |
|---|
| | ISO6603-2 | 8.00 J |
| | ISO6603-2 | 6.00 J |
| | ISO6603-2 | 950 N |
| | ISO6603-2 | 1070 N |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 4.00 |
| Dissipation Factor | | IEC60250 | 5E-03 |
| Dissipation Factor | | IEC60250 | 5E-03 |
| Dissipation Factor | | IEC60250 | 0.0150.015 |
| arc resistance | | ASTMD495 | -- sec |
| CTI | | ASTMD3638 | -- V |
| CTI | | IEC60112 | 600 V |
| CTI | | IEC60112 | 400 V |
| Surface Resistivity | | IEC60093 | 1E+14 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 40 KV/mm |
| dielectric strength | | IEC60243-1 | 40 KV/mm |
| dielectric constant | | IEC60250 | 4.00 |
| dielectric constant | | IEC60250 | 4.00 |
| | IEC60250 | 4.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 215 °C |
| | ASTMD648 | 200 °C |
| | ISO75-2/A | 200 °C |
| vicat | | ISO306/B50 | 200 °C |
| vicat | | ISO306/B120 | >200 °C |
| Melting temperature 5 | | ISO11357-3 | 222 °C |
| | ISO11359-2 | 2E-05 cm/cm/°C |
| | ISO11359-2 | 8E-05 cm/cm/°C |
| RTI Elec | | UL746 | 130 °C |
| RTI Imp | | UL746 | 95.0 °C |
| | ASTMD648 | 215 °C |
| RTI Imp | | UL746 | 95.0 °C |
| RTI Str | | UL746 | 130 °C |
| RTI Str | | UL746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices