Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| saturation | | % | 1.8到4.0 |
| Flow: | | mm/mm | 71.1E-3到0.635 |
| Balance, | | % | 0.37到1.7 |
| Water absorption rate | | | 1.07到1.08 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | Mpa | 35.03到129.66 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | Mpa | 34.83到65.24 |
| yield | | % | 4.5到6.9 |
| fracture | | % | 2.4到300 |
| fracture | | % | 3.0到54 |
| fracture | | Mpa | 30.9到110.34 |
| Bending stress | | Mpa | 22.0到95.86 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 0.882到3.992 |
| Impact strength of simply supported beam without notch | | kJ/m² | 17.642到22.286 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | V | 599到600 |
| Surface Resistivity | | ohms | 1.0E+10到2.5E+14 |
| Volume resistivity | | ohms·cm | 1.0E+11到1.5E+12 |
| dielectric strength | | V/mil | 760到1100 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 112到160 |
| melting temperature | | °C | 215到225 |
| horizontal | | mm/mm/°C | 111.8E-5到203.2E-5 |
| flow | | mm/mm/°C | 27.9E-5到25.4E-5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare