Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.16 g/cm³ |
Shrinkage rate | | 内部方法 | 0.30to0.50 % |
Water absorption rate | | ASTM D570 | 0.070 % |
Water absorption rate | | ASTM D570 | 0.22 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 104 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-1 |
Limiting Oxygen Index | | ASTM D2863 | 31 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | Break | ASTM D638 | 74.5 MPa |
elongation | Break | ASTM D638 | 5.0 % |
Flexural modulus | | ASTM D790 | 4000 MPa |
bending strength | | ASTM D790 | 120 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 69 J/m |
Impact strength of cantilever beam gap | | ASTM D256 | 96 J/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Dissipation Factor | | ASTM D150 | 1.6E-03 |
Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
dielectric constant | | ASTM D150 | 3.00 |
dielectric constant | | ASTM D150 | 3.00 |
dielectric constant | | ASTM D150 | 3.00 |
Dissipation Factor | | ASTM D150 | 1.7E-03 |
Dissipation Factor | | ASTM D150 | 1.7E-03 |
Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
High arc combustion index (HAI) | | UL 746 | PLC 2 |
High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 4 |
Hot wire ignition (HWI) | | UL 746 | PLC 1 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
RTI Elec | | UL 746 | 110 °C |
Heat distortion temperature | | ASTM D648 | 132 °C |
vicat | | ASTM D15255 | 148 °C |
RTI Imp | | UL 746 | 105 °C |
RTI | | UL 746 | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.