PA66 AR218V30 BK SOLVAY SHANGHAI

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceGlass fiber reinforcedenhance

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

High impact resistance | Glass fiber reinforced | enhance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	6.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6 mm	UL 94	HB
Burning wire flammability index	1.6 mm	IEC 60695-2-12	650	°C
Extreme Oxygen Index		ISO 4589-2	23	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1A	9900	Mpa
tensile strength	Break, 23°C	ISO 527-2/1A	150	Mpa
Tensile strain	Break, 23°C	ISO 527-2	2.4	%
Bending modulus	23°C	ISO 178	7000	Mpa
bending strength	23°C	ASTM D790	220	Mpa
bending strength	bending strength	23°C	ISO 178	200	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
Suggested maximum moisture content			0.20	%
Temperature at the rear of the barrel			270 to 280	°C
Temperature in the middle of the barrel			275 to 285	°C
Temperature at the front of the material cylinder			280 to 290	°C
Mold temperature			70 to 100	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	240	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	235	°C
Melting temperature		ISO 11357-3	260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24 hr, 23°C	ISO 62	0.80	%
	Water absorption rate	Saturation, 23°C	ISO 62	5.3	%
	Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.7	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.