Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 0.910 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 43 g/10min |
| Shrinkage rate | | ASTM D955 | 1.4 % |
| Shrinkage rate | | ASTM D955 | 1.4 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 75 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 28.4 MPa |
| tensile strength | Break | ASTM D638 | 17.7 MPa |
| Flexural modulus | | ASTM D790 | 1230 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 29 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 39 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 64 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTM D2117 | 120to163 °C |
| Heat distortion temperature | | ASTM D648 | 110 °C |
| Heat distortion temperature | | ASTM D648 | 55.0 °C |
| brittle temperature | | ASTM D746 | -20.0 °C |
| vicat | | ASTM D1525 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.