ABS KRALASTIC® ANG-20 BK901
22
- Usages:Home appliance components
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | GB/T2914 | 0.02 % | |
| GB/T2914 | 0.02 % | ||
| GB/T2914 | 0.02 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | GB/T1040 | 200 Mpa | |
| elongation at break | GB/T1040 | 1.8 % | |
| bending strength | GB/T9341 | 280 Mpa | |
| Flexural modulus | GB/T9341 | 1.4×10⁴ Mpa | |
| Impact strength of cantilever beam gap | GB/T1843 | 13 kJ/m² | |
| tensile strength | GB/T1040 | 200 Mpa | |
| elongation at break | GB/T1040 | 1.8 % | |
| bending strength | GB/T9341 | 280 Mpa | |
| Flexural modulus | GB/T9341 | 1.4×10⁴ Mpa | |
| Impact strength of cantilever beam gap | GB/T1843 | 13 kJ/m² | |
| tensile strength | GB/T1040 | 200 Mpa | |
| elongation at break | GB/T1040 | 1.8 % | |
| bending strength | GB/T9341 | 280 Mpa | |
| Flexural modulus | GB/T9341 | 1.4×10⁴ Mpa | |
| Impact strength of cantilever beam gap | GB/T1843 | 13 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | GB/T1033 | 1.66 g/cm³ | |
| Mold Shrinkage | GB/T15585 | 0.25/0.75 % | |
| density | GB/T1033 | 1.66 g/cm³ | |
| Mold Shrinkage | GB/T15585 | 0.25/0.75 % | |
| density | GB/T1033 | 1.66 g/cm³ | |
| Mold Shrinkage | GB/T15585 | 0.25/0.75 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | 5 ×10¹⁵Ω·M | ||
| Surface Resistivity | 5 ×10¹⁴Ω | ||
| dielectric constant | 4 1MHz | ||
| electric strength | GB/T1408 | 20 KV/mm | |
| Volume resistivity | 5 ×10¹⁵Ω·M | ||
| Surface Resistivity | 5 ×10¹⁴Ω | ||
| dielectric constant | 4 1MHz | ||
| electric strength | GB/T1408 | 20 KV/mm | |
| Volume resistivity | 5 ×10¹⁵Ω·M | ||
| Surface Resistivity | 5 ×10¹⁴Ω | ||
| dielectric constant | 4 1MHz | ||
| electric strength | GB/T1408 | 20 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting point | GB/T4608 | 285 °C | |
| Heat distortion temperature | GB/T1634 | 267 °C | |
| Flame retardancy | GB/TUL94 | V-0 | |
| melting point | GB/T4608 | 285 °C | |
| Heat distortion temperature | GB/T1634 | 267 °C | |
| Flame retardancy | GB/TUL94 | V-0 | |
| melting point | GB/T4608 | 285 °C | |
| Heat distortion temperature | GB/T1634 | 267 °C | |
| Flame retardancy | GB/TUL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.