Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | | 1.16到1.50 |
| Water absorption rate | | % | 0.020到0.16 |
| Shrinkage rate | | mm/mm | 101.6E-3到1.016 |
| K-Value | | | 56.5到80.3 |
| | ml/g | 83.1到161.4 |
| melt mass-flow rate | | g/10min | 6.2到7.0 |
| Apparent density | | | 1.16到1.50 |
| Water absorption rate | | % | 0.020到0.16 |
| melt mass-flow rate | | g/10min | 6.2到7.0 |
| Shrinkage rate | | mm/mm | 101.6E-3到1.016 |
| K-Value | | | 56.5到80.3 |
| | ml/g | 83.1到161.4 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | | 12到108 |
| | | 12到108 |
| | | 48到97 |
| | | 48到97 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | % | 1.5到3.0 |
| transmissivity | | % | 88.8到90.1 |
| Haze ratio | | % | 1.5到3.0 |
| transmissivity | | % | 88.8到90.1 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | mm/min | 4.318到6.35 |
| burning rate | | mm/min | 4.318到6.35 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | Mpa | 8.0到42.76 |
| fracture | | Mpa | 4.0到20.83 |
| fracture | | Mpa | 5.52到32.14 |
| yield | | Mpa | 32.97到62.0 |
| yield | | Mpa | 55.38到94.48 |
| fracture | | % | 200到410 |
| fracture | | % | 180到470 |
| yield | | Mpa | 8.0到42.76 |
| fracture | | Mpa | 4.0到20.83 |
| yield | | % | 290到460 |
| fracture | | Mpa | 5.52到32.14 |
| yield | | Mpa | 32.97到62.0 |
| yield | | Mpa | 55.38到94.48 |
| fracture | | % | 200到410 |
| fracture | | % | 180到470 |
| yield | | % | 290到460 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | kJ/m² | 2.414到5.572 |
| | kJ/m² | 2.414到4.643 |
| | N.m/mil | 12.57到53.10 |
| Impact strength of cantilever beam gap | | kJ/m² | 1.582到14.532 |
| Impact strength of cantilever beam gap | | kJ/m² | 1.582到14.532 |
| Impact strength of simply supported beam without notch | | kJ/m² | 2.414到5.572 |
| | kJ/m² | 2.414到4.643 |
| | N.m/mil | 12.57到53.10 |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | % | 100到120 |
| Water vapor permeability | | g/100 | 0.17到0.25 |
| tensile strength | Yield | Mpa | 49.66到60.83 |
| elongation | Break | % | 100到120 |
| Water vapor permeability | | g/100 | 0.17到0.25 |
| tensile strength | Yield | Mpa | 49.66到60.83 |
| Test Condition | Test Method | Test Result |
|---|
| tensile strength | | Mpa | 7.86到23.59 |
| compression set | | % | 47到48 |
| tensile strength | | Mpa | 7.86到23.59 |
| elongation | | % | 220到390 |
| compression set | | % | 47到48 |
| elongation | | % | 220到390 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | V/mil | 340到1000 |
| Volume resistivity | | | 2.75到3.40 |
| dielectric strength | | V/mil | 340到1000 |
| Volume resistivity | | | 2.75到3.40 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 59到105 |
| | mm/mm/°C | 88.9E-5到101.6E-5 |
| Continuous use temperature | | °C | 59到105 |
| | mm/mm/°C | 88.9E-5到101.6E-5 |
| melting temperature | | °C | 158到185 |
| brittle temperature | | °C | -50到-4 |
| melting temperature | | °C | 158到185 |
| brittle temperature | | °C | -50到-4 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.