PP Bolv PP 02003
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D1505 | 0.900 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 0.30 g/10min | |
| density | ASTM D1505 | 0.900 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 0.30 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | Break | ASTM D638 | 320 % |
| Flexural modulus | ASTM D790 | 950 MPa | |
| elongation | Break | ASTM D638 | 320 % |
| Flexural modulus | ASTM D790 | 950 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 90 J/m | |
| ASTM D256 | 90 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | ASTM D149 | 45 kV/mm | |
| ASTM D149 | 45 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 160 °C | ||
| vicat | ASTM D1525 | 140 °C | |
| ASTM D1525 | 140 °C | ||
| melting temperature | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.