PPS F4-HGR313
29
- Properties:Flame retardantHigh temperature resistanwear resistantGlass fiber reinforcedCorrosion resistance
- Usages:Automotive sectorIndustrial machineryHousehold appliances
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | GB/T 15585-1995 | 0.0025 mm/mm |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | GB/T 1033-1986 | 1.58 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | GB/T 1040-1992 | 138 Mpa | |
| Flexural modulus | GB/T 1042-1992 | 1.0×104 Mpa | |
| bending strength | GB/T 1042-1992 | 200 Mpa | |
| Impact strength of cantilever beam gap | GB/T 1843-1996 | 12.9 kJ/m² |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| GB/T 3690-1983 | 0.35 | ||
| Wear scar width | GB/T 3690-1983 | 5.5 mm | |
| Wear amount | GB/T 3690-1983 | 4.5 mg/120min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | GB/T 1634-1979 | 272 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.