Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.40 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 0.55 % |
| Water absorption rate | | ISO 62 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1A | 21000 Mpa |
| Tensile stress | | ISO 527-2/1A | 240 Mpa |
| Tensile strain | | ISO 527-2 | 2.3 % |
| Flexural modulus | | ISO 178 | 19500 Mpa |
| Bending stress | | ISO 178 | 380 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 85 kJ/m² |
| | ISO 180/1U | 90 kJ/m² |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Suggested maximum moisture content | | | 0.20 % |
| Temperature at the rear of the barrel | | | 230 到 235 °C |
| Temperature in the middle of the barrel | | | 235 到 245 °C |
| Temperature at the front of the material cylinder | | | 245 到 250 °C |
| Temperature | | | 60 到 90 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/Af | 215 °C |
| melting temperature | | ISO 11357-3 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.