POM/GF/PTFE LNP™ LUBRICOMP™ KFL4036 SABIC INNOVATIVE US
43
- Properties:High temperature resistanUV resistance
- Usages:Castershousehold electrical appliances
Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|---|---|---|
Shrinkage rate | ASTM D955 | 0.70-1.0 % | |
ASTM D955 | 1.0-3.0 % | ||
Water absorption rate | ASTM D570 | 0.16 % | |
ISO 62 | 0.26 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
tensile strength | ASTM D638 | 88.0 Mpa | |
ISO 527-2/5 | 84.0 Mpa | ||
elongation | ASTM D638 | 1.3 % | |
Tensile strain | ISO 527-2/5 | 1.3 % | |
Flexural modulus | ASTM D790 | 9280 Mpa | |
ISO 178 | 9930 Mpa | ||
bending strength | ISO 178 | 130 Mpa | |
ASTM D790 | 107 Mpa | ||
coefficient of friction | ASTM D3702Modified | 0.40 | |
ASTM D3702Modified | 0.46 | ||
Tensile modulus | ASTM D638 | 10800 Mpa | |
ISO 527-2/1 | 10600 Mpa | ||
Wear factor | ASTM D3702Modified | 235 10^-10in^5-min/ft-lb-hr |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of cantilever beam gap | ISO 180/1A | 5.9 kJ/m² | |
Suspended wall beam without notch impact strength | ISO 180/1U | 25 kJ/m² | |
Dart impact | ASTM D3763 | 10.3 J | |
Multi axis Instrumented Impact Energy | ISO 6603-2 | 2.50 J |
Thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Linear coefficient of thermal expansion | ASTM D696 | 9.5E-05 cm/cm/°C | |
ASTM D696 | 6.5E-05 cm/cm/°C | ||
Heat distortion temperature | ASTM D648 | 183 °C | |
ISO 75-2/Bf | 163 °C | ||
ASTM D648 | 161 °C | ||
ISO 75-2/Af | 161 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.