Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.00 g/cm³ |
| melt mass-flow rate | | ISO1133 | 10 g/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2 | 20.0 MPa |
| Tensile strain | Break | ISO527-2 | 40 % |
| Flexural modulus | | ISO178 | 1700 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180 | 8.5 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180 | 20 kJ/m² |
| aging | Test Condition | Test Method | Test Result |
|---|
| AcceleratedAging | | 内部方法 | 6.3 day |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 53.0 °C |
| vicat | | ISO306/B | 55.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.