Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.36 g/cm³ |
| melt mass-flow rate | | ISO1133 | 11 g/10min |
| Shrinkage rate | | ISO294-4 | 1.0 % |
| Shrinkage rate | | ISO294-4 | 1.0 % |
| Water absorption rate | | ISO62 | 0.030 % |
| Ash Content | | ISO3451 | 52 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 74 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO527-2/20 | 5.0 % |
| Tensile strain | | ISO527-2/20 | 15 % |
| Tensile stress | | ISO527-2/20 | 15.0 MPa |
| Tensile stress | | ISO527-2/20 | 13.0 MPa |
| Flexural modulus | | ISO178 | 2500 MPa |
| Bending stress | | ISO178 | 25.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 20 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 2.5 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 94.0 °C |
| | ISO75-2/A | 56.0 °C |
| vicat | | ISO306/A50 | 140 °C |
| vicat | | ISO306/B50 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.