PET 415HP-NC010 DUPONT JAPAN

Form：Granules | Grade：Enhanced level

Properties:

High impact resistanceFiller: Glass fiber reinf15% filler by weight

Typical Applications:

Fitness equipmentAutomotive Applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Fitness equipment \| Automotive Applications
Properties:	High impact resistance \| Filler: Glass fiber reinf \| 15% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	25	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	55	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	<100	mm/min
UL flame retardant rating	0.75mm	UL 94,IEC60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94,IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	19	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	4700	Mpa
tensile strength	Break	ISO 527-2	79.0	Mpa
Tensile strain	Break	ISO 527-2	5.0	%
Bending modulus		ISO 178	3550	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	235	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	207	°C
Vicat softening temperature		ISO 306/B50	205	°C
Melting temperature		ISO 11357-3	250	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:-40to23°C	ISO 11359-2	9.8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD:55to160°C	ISO 11359-2	1.1E-04	cm/cm/°C
			Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04	cm/cm/°C
				Linear coefficient of thermal expansion	TD:-40to-23°C	ISO 11359-2	4E-05	cm/cm/°C
					Linear coefficient of thermal expansion	TD:55to160°C	ISO 11359-2	3.2E-05	cm/cm/°C
					Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	EffectiveThermalDiffusivity	ISO 11359-2	9E-08	m²/s
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	ISO 294-4	0.80	%
	Shrinkage rate	TD3	ISO 294-4	1.2	%
		Shrinkage rate	MD	ISO 294-4	0.30	%
		Shrinkage rate	Shrinkage rate	MD3	ISO 294-4	0.50	%
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	2.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.25	%
Melt Volume Flow Rate (MVR)	280°C/2.16kg	ISO 1133	4.00	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+13	ohms·cm
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	PLC 2
Surface resistivity		IEC 60093	1E+13	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ISO 2039-2	58
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	111

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.