Other performance	Test Condition	Test Method	Test Result	Test Unit
Loss angle	100HZ		10
Extreme Oxygen Index			15	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃/10kg		7.5	CM
density			1400	kg/cm
Water absorption rate			0.2	%
Water absorption rate	Water absorption rate			0.8	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	1h		1800	Mpa
elongation at yield			9.6	%
Charpy Notched Impact Strength	23℃		200	KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃		5.5	KJ/m
Tensile modulus			2600	Mpa
tensile strength	Yield		63	Mpa
elongation	Break		29	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.6mm		HB	CLASS
Hot deformation temperature	1.80MPa		105	°C
Vicat softening temperature	50℃/h50n		150	°C
Melting temperature	10℃/min		167	°C
Linear coefficient of thermal expansion	水平方向		1.1	E-4/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	水平方向		2.1	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity			1E+13	Ohm
Dielectric strength			40	KV/mm
Dielectric constant	100HZ		3.8
Volume resistivity			1E+13	Ohm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.