PA6 9B22135 4Plas

Properties:

Filler glass fiber reinforced material 35% filler by weight

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Filler | glass fiber reinforced material | 35% | filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	14	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	17	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	650	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break,23°C	ISO 527-2/5	3.0	%
Impact strength of cantilever beam gap	23°C	ISO 180/1A	17	kJ/m²
Tensile modulus	23°C	ISO 527-2/5	10500	MPa
tensile strength	Break,23°C	ISO 527-2/5	185	MPa
Tensile modulus	23°C	ISO 527-2/5	10500	MPa
tensile strength	Break, 23°C	ISO 527-2/5	185	MPa
Tensile strain	Break,23°C	ISO 527-2/5	3.0	%
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	14	kJ/m²
Heat distortion temperature	Test Condition	Test Method	Test Result	Test Unit
Electrical Properties	漏电起痕指数	IEC 60112	500	V
Hot deformation temperature	可燃性，UL 阻燃等级	UL 94	HB	1.60 mm
Hot deformation temperature	Hot deformation temperature	热灯丝点火温度，2.00 mm	IEC 60695-2-13	650	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306/B	215	°C
Melting temperature		ISO 11357	223	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220	°C
	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	220	°C
		Hot deformation temperature	维卡软化温度	ISO 306/B	215	°C
		Hot deformation temperature	Hot deformation temperature	Melting Temperature	ISO 11357	223	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.40	g/cm³
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.9	%
density		ISO 1183	1.40	g/cm³
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.9	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.