Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.53 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 1.4 % |
| Shrinkage rate | | ISO 294-4 | 2.0 % |
| Water absorption rate | | ISO 62 | 1.0 % |
| MediumDensity | | | 1.28 g/cm³ |
| Water absorption rate | | ISO 62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 83 |
| Rockwell hardness | | ISO 2039-2 | 119 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | <100 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | | FMVSS302 | B |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2800 Mpa |
| tensile strength | | ISO 527-2 | 50.0 Mpa |
| Tensile strain | | ISO 527-2 | 10 % |
| Flexural modulus | | ISO 178 | 2500 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 35 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 40 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 3.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 160 °C |
| Heat distortion temperature | | ISO 75-2/A | 92.0 °C |
| melting temperature | | ISO 11357-3 | 178 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1E-04 cm/cm/°C |
| AnnealingTemperature | | | 160 °C |
| AnnealingTime-Optional | | | 30.0 min/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.