Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.14 -- |
| Shrinkage rate | | % | 1.2到1.6 -- |
| Water absorption rate | | % | 1.3 -- |
| HeatStability | | °C | 80 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 120 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-2 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 2900 1300 |
| tensile strength | | MPa | 75.0 50.0 |
| elongation | | % | 50 120 |
| Flexural modulus | | MPa | 2900 1000 |
| bending strength | | MPa | 100 40.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | J/m | 45 85 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 18 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 170 -- |
| | °C | 75.0 -- |
| melting temperature | | °C | 214到220 -- |
| | cm/cm/°C | 7E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare