Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.80 -- |
| Water absorption rate | | % | 1.5 -- |
| Water absorption rate | | % | 0.70 -- |
| density | | g/cm³ | 1.01 -- |
| Shrinkage rate | | % | 1.2 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 67 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 600 -- |
| tensile strength | Yield | MPa | 35.0 -- |
| tensile strength | Break | MPa | 40.0 -- |
| Tensile strain | Yield | % | 15 -- |
| Tensile strain | Break | % | >50 -- |
| Nominal tensile fracture strain | | % | >50 -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 95 -- |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Charpy Notched Impact Strength | | kJ/m² | 7.0 -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | -- 1E+13 |
| dielectric strength | | kV/mm | 32 -- |
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 150 -- |
| melting temperature | | °C | 175 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.3E-04 -- |
| Heat distortion temperature | | °C | 115 -- |
| Heat distortion temperature | | °C | 45.0 -- |
| Continuous use temperature | | °C | 80.0to120 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.6E-04 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.