PA6

PA6 MAZMID B 150 FV 20 Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda.

Properties:
Filler glass fiber reinforced material 20% filler by weight
Usages:
Electrical electronic applications knobs electrical components automotive applications casings gears
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		J/m	90 150

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm		HB --

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		MPa	6000 3500
tensile strength		MPa	120 75.0
elongation	Break	%	4.0 6.0
Bending modulus		MPa	6000 3500
bending strength		MPa	190 100

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	°C	200 --
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	°C	180 --
Continuous use temperature		°C	90.0to100 --
Melting temperature		°C	214to220 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	3E-05 --

Physical properties	Test Condition	Test Method	Test Result
density		g/cm³	1.25 --
Shrinkage rate	MD	%	0.40to0.60 --
Water absorption rate	23°C,24hr	%	1.1 --

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ohms·cm	1E+15 --
Dielectric strength		kV/mm	22 --

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale		122 110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.