Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.990 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 14 g/10min |
| Shrinkage rate | | 内部方法 | 1.1 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| atomization | | DIN 75201 | 2.5E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA277 | 35.0 µgC/g |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 25 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 110 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | | ISO 180/1A | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 27 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 72 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ISO 527-2/1 | 1700 MPa |
| tensile strength | | ISO 527-2/50 | 20.0 MPa |
| Tensile strain | | ISO 527-2/50 | 4.0 % |
| Flexural modulus | Injection | ISO 178 | 1750 MPa |
| bending strength | Injection | ISO 178 | 30.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| MeltEnergy | | ISO 11357 | 64.1 kJ/kg |
| Heat distortion temperature | | ISO 75-2/B | 97.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 54.0 °C |
| vicat | | ISO 306/A50 | 140 °C |
| vicat | | ISO 306/B50 | 54.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.