PC/ABS C2800 SABIC INNOVATIVE US

Form：Granules | Grade：Injection grade

Properties:

Flame retardantHigh mobilityHigh impact resistance

Typical Applications:

Electrical fieldElectronic fieldHousehold appliancesHousehold appliancesAutomotive sector

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Household appliances \| Household appliances \| Automotive sector
Properties:	Flame retardant \| High mobility \| High impact resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ASTM D256	430	J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	58.3	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	2.31mm	UL 94	5VB
Extreme Oxygen Index		ASTM D2863	35	%
UL flame retardant rating	0.889mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	1.47mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2690	Mpa
elongation	Break	ASTM D638	50	%
Bending modulus	100mmSpan	ASTM D790	2690	Mpa
bending strength	Yield,100mmSpan	ASTM D790	96.5	Mpa
tensile strength	Yield	ASTM D638	58.6	Mpa
elongation	Yield	ASTM D638	5.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:-40to60°C	ASTME831	7.2E-05	cm/cm/°C
thermal conductivity		ASTMC177	0.20	W/m/K
RTI Elec		UL 746	80.0	°C
RTI Imp		UL 746	70.0	°C
RTI		UL 746	80.0	°C
Linear coefficient of thermal expansion	MD:-40to60°C	ASTME831	7.2E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	73.9	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	80.0	°C
Vicat softening temperature		ASTM D15257	90.6	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	--	ASTM D792	1.17	g/cm³
density	density	--1	ASTM D792	1.18	g/cm³
melt mass-flow rate	260°C/2.16kg	ASTM D1238	16	g/10min
Shrinkage rate	MD:3.20mm	Internal Method	0.40-0.60	%
Shrinkage rate	Shrinkage rate	TD:3.20mm	Internal Method	0.40-0.60	%
Water absorption rate	24hr	ASTM D570	0.10	%
Water absorption rate	Water absorption rate	Equilibrium,23°C	ASTM D570	0.40	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	100Hz	ASTM D150	3.00
Dissipation factor	50Hz	ASTM D150	4.8E-03
Dissipation factor	Dissipation factor	60Hz	ASTM D150	4.8E-03
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 1
High arc combustion index	HAI	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 3
Surface resistivity		ASTM D257	>1.0E+14	ohms
Volume resistivity		ASTM D257	1E+17	ohms·cm
Dielectric strength	3.20mm,inOil	ASTM D149	18	KV/mm
Dielectric constant	50Hz	ASTM D150	3.00
Dielectric constant	Dielectric constant	60Hz	ASTM D150	3.00
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App