Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.36 g/cm³ |
spiral flow length | | 内部方法 | 66.0 cm |
Shrinkage rate | | ISO 294-4 | 0.70 % |
Shrinkage rate | | ISO 294-4 | 0.30 % |
Water absorption rate | | ISO 62 | 6.3to6.9 % |
Water absorption rate | | ISO 1110 | 2.1to2.3 % |
hardness | Test Condition | Test Method | Test Result |
---|
ball-indentation hardness | | ISO 2039-1 | 230 MPa |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | HB |
Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
burning rate | | FMVSS302 | <100 mm/min |
Supplementary Information | Test Condition | Test Method | Test Result |
---|
ReinforcementContent | | ISO 1172 | 30 % |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | Break | ISO 527-2/5 | 170 MPa |
Tensile strain | Break | ISO 527-2/5 | 3.0 % |
Flexural modulus | | ISO 178 | 8500 MPa |
bending strength | | ISO 178 | 270 MPa |
Tensile modulus | | ISO 527-2/1 | 10000 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of simply supported beam without notch | | ISO 179/1eU | 80 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | IEC 60093 | 1E+12 ohms |
Volume resistivity | | IEC 60093 | 1E+13 ohms·cm |
Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/A | 210 °C |
Heat distortion temperature | | ISO 75-2/C | 150 °C |
melting temperature | | DIN EN11357-1 | 220 °C |
Heat distortion temperature | | ISO 75-2/B | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.