Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.36 g/cm³ |
| Shrinkage rate | | ISO294-4 | 0.30到0.60 % |
| Shrinkage rate | | ISO294-4 | 0.40到0.70 % |
| Shrinkage rate | | ISO294-4 | <0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 75 |
| Rockwell hardness | R-Scale | ISO2039-2 | 112 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 200 MPa |
| Tensile stress | Break | ISO527-2 | 130 MPa |
| Tensile strain | Break | ISO527-2 | 4.0 % |
| Flexural modulus | | ISO178 | 6000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180 | 8.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 1E+11 ohms |
| Volume resistivity | | ASTMD257 | 1E+12 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 190 °C |
| melting temperature | | ISO11357-3 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare