PA66 A 50H1 SOLVAY SHANGHAI
26
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 1.3 % | |
| ISO 294-4 | 1.5 % | ||
| Water absorption rate | ISO 62 | 0.88 % | |
| ISO 62 | 2.7 % | ||
| Outdoor applicability | UL 746C | f1 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | V-0 | ||
| UL 94 | V-0 | ||
| UL 94 | V-0 | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| IEC 60695-2-12 | 960 °C | ||
| IEC 60695-2-12 | 960 °C | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 960 °C | |
| IEC 60695-2-13 | 960 °C | ||
| IEC 60695-2-13 | 775 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 33 % | |
| European Railways Certifications | EN 45545-2 | HL3 | |
| EN 45545-2 | HL3 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 3800 Mpa | |
| Tensile stress | ISO 527-2/1A | 85.0 Mpa | |
| ISO 527-2/1A | 80.0 Mpa | ||
| Tensile strain | ISO 527-2 | 12 % | |
| Flexural modulus | ASTM D790 | 3800 Mpa | |
| ISO 178 | 3700 Mpa | ||
| bending strength | ASTM D790 | 125 Mpa | |
| ISO 178 | 135 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 90 kJ/m² | |
| ISO 179/1eU | 80 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 3.0E+15 ohms | |
| Volume resistivity | IEC 60093 | 3.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| IEC 60243-1 | 21 KV/mm | ||
| IEC 60250 | 3.50 | ||
| Dissipation Factor | IEC 60250 | 0.017 | |
| CTI | IEC 60112 | 600 V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Suggested maximum moisture content | 0.20 % | ||
| Temperature at the rear of the barrel | 260 到 270 °C | ||
| Temperature in the middle of the barrel | 265 到 275 °C | ||
| Temperature at the front of the material cylinder | 265 到 275 °C | ||
| Temperature | 60 到 80 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75-2/Bf | 237 °C | ||
| ISO 75-2/Af | 85.0 °C | ||
| melting temperature | ISO 11357-3 | 263 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.