Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.39 g/cm³ |
| Water absorption rate | | | 0.50 % |
| Water absorption rate | | | 0.50 % |
| Water absorption rate | | ISO 62 | 6.0 mg |
| Water absorption rate | | ISO 62 | 13.0 mg |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 96 |
| ball-indentation hardness | | ISO 2039-1 | 170 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3700 MPa |
| tensile strength | | ISO 527-2 | 90.0 MPa |
| Tensile strain | | ISO 527-2 | 15 % |
| Tensile creep modulus | | ISO 899-1 | 26.0 MPa |
| compression stress | | ISO 604 | 103 MPa |
| compression stress | | ISO 604 | 51.0 MPa |
| compression stress | | ISO 604 | 26.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | >50 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/2A | 2.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+14 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 22 kV/mm |
| relative permittivity | | IEC 60250 | 3.40 |
| relative permittivity | | IEC 60250 | 3.20 |
| Dissipation Factor | | IEC 60250 | 1E-03 |
| Dissipation Factor | | IEC 60250 | 0.014 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 75.0 °C |
| melting temperature | | | 255 °C |
| Linear coefficient of thermal expansion | | | 6E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 0.29 W/m/K |
| Linear coefficient of thermal expansion | | | -20 °C |
| maximum service temperature | | | 115 °C |
| maximum service temperature | | | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.