Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.14 -- |
| Water absorption rate | | % | 1.3 -- |
| melt mass-flow rate | | g/10min | 25to35 -- |
| Shrinkage rate | | % | 1.3to1.7 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 120 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-2 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 2800 1000 |
| tensile strength | | MPa | 70.0 40.0 |
| elongation | Break | % | >50 >150 |
| Flexural modulus | | MPa | 2800 1000 |
| bending strength | | MPa | 95.0 40.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 50 80 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 18 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 160 -- |
| Heat distortion temperature | | °C | 60.0 -- |
| Continuous use temperature | | °C | 80.0 -- |
| melting temperature | | °C | 214to220 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 7E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.