Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.26 -- |
| Water absorption rate | | % | 9.0to10 -- |
| Water absorption rate | | % | 2.5to3.4 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 120 102 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| UL flame retardant rating | | | V-2 -- |
| Hot filament ignition temperature | | °C | 750 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | MPa | 80.0 40.0 |
| tensile strength | Break | MPa | 60.0 30.0 |
| elongation | Break | % | >60 >200 |
| Flexural modulus | | MPa | 2800 800 |
| bending strength | | MPa | 120 60.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 45 500 |
| Suspended wall beam without notch impact strength | | J/m | 50 600 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | 1E+13 1E+10 |
| Volume resistivity | | ohms·cm | 1E+15 1E+11 |
| dielectric strength | | kV/mm | 90 40 |
| dielectric constant | | | 3.60 7.00 |
| Dissipation Factor | | | 0.030 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| thermal conductivity | | W/m/K | 0.25 -- |
| Heat distortion temperature | | °C | 180 -- |
| Heat distortion temperature | | °C | 70.0 -- |
| vicat | | °C | 200 -- |
| vicat | | °C | 165 -- |
| melting temperature | | °C | 215to220 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 7.5E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.