physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.2 g/cm³ |
Shrinkage rate | | ISO 294 | 0.50-0.70 % |
Shrinkage rate | | ISO 294 | 0.50-0.70 % |
Water absorption rate | | ISO 62 | 0.32 % |
Water absorption rate | | ISO 62 | 0.15 % |
melt mass-flow rate | | ISO 1133 | 10 g/10min |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ISO 2039 | 120 |
optical performance | Test Condition | Test Method | Test Result |
---|
transmissivity | | ISO 13468 | 89 % |
cleanliness | | ISO 14782 | 0.8 % |
refractive index | | ISO 489 | 1.586 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527 | 2400 Mpa |
tensile strength | | ISO 527 | 60 Mpa |
elongation | | ISO 527 | 6 % |
elongation | | ISO 527 | 150 % |
bending strength | | ISO 178 | 97 Mpa |
Flexural modulus | | ISO 178 | 2410 Mpa |
Impact strength of cantilever beam gap | | ISO 180 | 70 kJ/㎡ |
Suspended wall beam without notch impact strength | | ISO 180 | NB kJ/㎡ |
Charpy Notched Impact Strength | | ISO 179 | 75 kJ/㎡ |
Charpy Notched Impact Strength | | ISO 179 | NB kJ/㎡ |
Flame retardant performance | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | HB |
UL flame retardant rating | | UL 94 | HB |
GWIT | | IEC 60695 | 875 °C |
GWIT | | IEC 60695 | 875 °C |
Relative temperature of heating wire | | IEC 60695 | 875 °C |
Relative temperature of heating wire | | IEC 60695 | 960 °C |
Limiting Oxygen Index | | ISO 4589 | 27 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | IEC 60093 | 200000000000000000 Ω.cm |
Surface Resistivity | | IEC 60093 | 10000000000000000 Ω |
dielectric strength | | IEC 60243 | 34 KV/mm |
dielectric constant | | IEC 60250 | 3.1 |
dielectric constant | | IEC 60250 | 3 |
Dissipation Factor | | IEC 60250 | 0.001 |
Dissipation Factor | | IEC 60250 | 0.01 |
proof tracking index | | IEC 60112 | 250 V |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75 | 144 °C |
Heat distortion temperature | | ISO 75 | 128 °C |
vicat | | ISO 306 | 149 °C |
Glass Transition Temperature | | ISO 11357 | 149 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.