Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:100.按容量计算的混合比:100 |
| Thermosetting components | | | 按重量计算的混合比:40.按容量计算的混合比:38 |
| Thermosetting components | | | 26 wk |
| Thermosetting mixed viscosity | | Brookfield | 250 cP |
| Thermosetting mixed viscosity | | Brookfield | 2430 cP |
| Thermosetting mixed viscosity | | Brookfield | 120to180 min |
| Thermosetting mixed viscosity | | Brookfield | 4350 cP |
| Thermosetting mixed viscosity | | Brookfield | 8.0to10.0 min |
| Thermosetting mixed viscosity | | Brookfield | 12.0to15.0 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D2566 | 0.50 % |
| density | | | 1.12 g/cm³ |
| density | | | 1.17 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 65to75 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CureTime | | | 5.0to7.0 day |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | >470 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 372 MPa |
| bending strength | | ASTM D790 | 14.3 MPa |
| Flexural modulus | | ASTM D790 | 372 MPa |
| elongation | Break | ASTM D638 | 480 % |
| tensile strength | | ASTM D638 | 34.6 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 133 kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.