Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| water content | | ISO 15512 | <0.080 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| density | | ISO 1183 | 1.52 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC 60695-2-13 | 725 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 9.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 65 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 60 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO 527-2 | 3.0 % |
| tensile strength | | ISO 527-2 | 100 MPa |
| Tensile modulus | | ISO 527-2 | 7500 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 225to255 °C |
| Heat distortion temperature | | ISO 75-2/A | 175 °C |
| Heat distortion temperature | | ISO 75-2/B | 215 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare