PP Copolymer

PP Copolymer J-68/25/E/SD Canada Fiberfil

Properties:
Filler glass fiber reinforced material 25% filler by weight
Compare

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	Yield伸长率	ASTM D638	7.5 %
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	230 J/m
Bending modulus	23°C	ASTM D790	3500 MPa
bending strength	23°C	ASTM D790	71.98 MPa
Tensile modulus	23°C	ASTM D638	3620 MPa
tensile strength	Yield,23°C	ASTM D638	50.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.80MPaUnannealed	ASTM D648	135 °C
Hot deformation temperature	Hot deformation temperature	0.45MPaUnannealed	ASTM D648	143 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	收缩率	ASTM D995	0.40 %
	melt mass-flow rate	收缩率	ASTM D995	0.25 %
	melt mass-flow rate	melt mass-flow rate	℃/Kg	ASTM D1238	9.0-11 g/10min
Water absorption rate	(23°C,24hr)	ASTM D570	0.020 %
Shrinkage rate	TD,3.17mm	ASTM D995	0.30 %
Shrinkage rate	Shrinkage rate	MD,3.17mm	ASTM D995	0.15 %
density		ASTM D792	1.07 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	90 R

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.