Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Humidity Absorption | | ISO1110 | 0.80to0.90 % |
| density | | ISO1183 | 1.24 g/cm³ |
| Melt volume flow rate | | ISO1133 | 60.0 cm³/10min |
| SpiralFlow | | 内部方法 | 155 cm |
| Shrinkage rate | | ISO294-4 | 1.8 % |
| Shrinkage rate | | ISO294-4 | 1.8 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| FlameRating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 1900 MPa |
| Bending stress | | ISO178 | 70.0 MPa |
| Tensile modulus | | ISO527-2/1 | 1500 MPa |
| Tensile stress | Yield | ISO527-2/50 | 60.0 MPa |
| Tensile strain | Break | ISO527-2/50 | >200 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.5 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 600 V |
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | IEC60093 | 1E+13 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 85.0 °C |
| melting temperature | | DINEN11357-1 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.