PA66 A3EG6 BASF USA

Form：Granules | Grade：Enhanced level

Properties:

High rigidityOil resistantdimensional stability

Typical Applications:

machineMechanical componentsShellElectrical componentsElectronic insulation

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	machine \| Mechanical components \| Shell \| Electrical components \| Electronic insulation
Properties:	High rigidity \| Oil resistant \| dimensional stability

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	70	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	85	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB
Polymer Abbreviation			PA66-GF30
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	10000	Mpa
tensile strength	Break	ISO 527-2	190	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
Tensile creep modulus	1000 hr	ISO 899-1	--	Mpa
Bending modulus		ISO 178	8600	Mpa
bending strength		ISO 178	280	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Processing (melt) temperature			280 to 300	°C
Mold temperature			80 to 90	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	250	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	250	°C
Melting temperature		ISO 11357-3	260	°C
specific heat			1500	J/kg/°C
thermal conductivity		DIN 52612	0.35	W/m/K
Temperature index - at 50% loss of tensile strength	--5	IEC 60216	165	°C
Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength	--6	IEC 60216	135	°C
Maximum operating temperature	短周期操作		240	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Apparent density			0.70	g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0 kg	ISO 1133	40.0	cm3/10min
Water absorption rate	Saturation, 23°C	ISO 62	5.2 to 5.8	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.5 to 1.9	%
Stickiness	96% H2SO4	ISO 307	145	cm³/g
Mold Shrinkage - Constrained			0.55	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	--	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Relative permittivity	1 MHz	IEC 60250	3.50
Dissipation factor	1 MHz	IEC 60250	0.014

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.