TPU-Est/eth DP R 3932

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO1183/A	1.38 g/cm³
Shrinkage rate			0.16 %
Shrinkage rate	Shrinkage rate			0.58 %

hardness	Test Condition	Test Method	Test Result
		ISO868	72

Mechanical properties	Test Condition	Test Method	Test Result
Abrasion		ISO4649	61 mm³
Tensile stress		ISO527-2/200	83.0 MPa
Tensile strain	Break	ISO527-2/200	11 %
Flexural modulus		ISO178	6220 MPa
Flexural modulus	Flexural modulus		ISO178	3200 MPa
Bending stress		ISO178	227 MPa
Bending stress	Bending stress		ISO178	99.0 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO179/1eA	9.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179/1eA	24 kJ/m²
Impact strength of simply supported beam without notch		ISO179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO179/1eU	92 kJ/m²

Thermal performance	Test Method	Test Result
	ISO75-2/B	159 °C
		ISO75-2/A	130 °C
vicat	ISO306/B50	146 °C
	DIN53752	2.1E-05 cm/cm/°C
		DIN53752	1.3E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.