Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.30 g/cm³ |
| Shrinkage rate | | | 1.3 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 99 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | 内部方法 | 0.160 kPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 4.5 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 4.7 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 170 MPa |
| compression stress | | ISO 604 | 135 MPa |
| shear modulus | | ISO 15310 | 1000 MPa |
| shear strength | | ASTM D732 | 88.0 MPa |
| Poisson's ratio | | ASTM D638 | 0.36 |
| tensile strength | Yield | ISO 527-2 | 108 MPa |
| tensile strength | | ISO 527-2 | 115 MPa |
| Tensile strain | Break | ISO 527-2 | 25 % |
| Tensile strain | | ISO 527-2 | 20 % |
| Flexural modulus | | ISO 178 | 4200 MPa |
| Flexural modulus | | ISO 178 | 4000 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI | | UL 746 | 260 °C |
| melting temperature | | | 340 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 4.7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.1E-04 cm/cm/°C |
| RTI Elec | | UL 746 | 260 °C |
| RTI Imp | | UL 746 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.