Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | 内部方法 | 1.82 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.22 % |
| Shrinkage rate | | 内部方法 | 0.45 % |
| Water absorption rate | | ISO62 | 0.010 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ISO11443 | 200 Pa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | 内部方法 | 120 MPa |
| elongation | Break | 内部方法 | 1.2 % |
| Flexural modulus | | 内部方法 | 9500 MPa |
| bending strength | | 内部方法 | 220 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+16 ohms |
| Volume resistivity | | IEC60093 | 3E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 20 kV/mm |
| dielectric constant | | IEC60250 | 5.20 |
| dielectric constant | | IEC60250 | 5.20 |
| Dissipation Factor | | IEC60250 | 2E-03 |
| Dissipation Factor | | IEC60250 | 2E-03 |
| CTI | | IEC60112 | 150 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | 内部方法 | 265 °C |
| | ISO11359-2 | 2E-05 cm/cm/°C |
| | ISO11359-2 | 3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.