SPS XAREC™ C122 IDEMITSU JAPAN
367
- Properties:High temperature resistanGlass fiber reinforced
- Usages:Household daily necessitiElectrical applications
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.11 | ||
| Shrinkage rate | ASTM D955 | MD 0.4～0.7 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.01 | % | |
| Shrinkage rate | TD | 内部方法 | 0.50to0.80 | % |
| MD | 内部方法 | 0.40to0.70 | % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.010 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 5400 | Mpa | |
| tensile strength | 断裂 | ISO527-2 | 75.0 | Mpa |
| elongation | 断裂 | ISO527-2 | 2.7 | % |
| Bending modulus | ISO178 | 5000 | Mpa | |
| bending strength | ISO178 | 120 | Mpa | |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 35 | kJ/m² |
| Cantilever beam without notch impact strength | 23°C | ISO180 | 30 | kJ/m² |
| elongation at break | ASTM D638/ISO 527 | 2.7 | % | |
| tensile strength | ASTM D638/ISO 527 | 75 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 45 | ||
| Bending modulus | ASTM D790/ISO 178 | 5 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 120 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB/0.80 | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | MD 3 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 260 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 140 | °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | TMA | 3E-05 | cm/cm/°C |
| TD：-30to30°C | TMA | 8.1E-05 | cm/cm/°C | |
| RTIElec | UL746 | 50.0 | °C | |
| RTI Imp | UL746 | 50.0 | °C | |
| RTIStr | UL746 | 50.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+16 | ohms·cm | |
| Dielectric strength | ASTMD149 | 45 | KV/mm | |
| Dielectric constant | 1MHz | IEC60250 | 2.80 | |
| Dissipation factor | 1MHz | IEC60250 | <1.0E-3 | |
| Arc resistance | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI)3 | IEC60112 | PLC0 | |
| Arc resistance | ASTM D495/IEC 60112 | 105 | ||
| Volume resistivity | ASTM D257/IEC 60093 | >1.0*10^16 | Ω.cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | >0.8mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.