Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.03 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.70to0.90 % |
| density | | ASTM D792 | 1.03 g/cm3 |
| Shrinkage rate | | ASTM D955 | 0.70-0.90 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 94 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTM D638 | 37.2 MPa |
| elongation | Yield | ASTM D638 | 25 % |
| Flexural modulus | | ASTM D790 | 1930 MPa |
| bending strength | | ASTM D790 | 65.5 MPa |
| Rockwell hardness | | ASTM D785 | 94 R 计秤 |
| Fracture tensile strength | | ASTM D638 | 37.2 MPa |
| elongation at yield | | ASTM D638 | 25 % |
| Flexural modulus | | ASTM D790 | 1930 MPa |
| bending strength | | ASTM D790 | 65.5 MPa |
| Impact strength of cantilever beam gap | | ASTM D256 | 530 J/m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 530 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 85.0 °C |
| Heat distortion temperature | | ASTM D648 | 85.0 ℃ |
| UL flame retardant rating | | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare