HDPE

HDPE C BK USA TPC

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	3.18 mm	ASTM D-256	267 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Basic Performance	Test Condition	Test Method	Test Result
density		ASTM D792	1.06 g/cm3
Water absorption rate	24hr	ASTM D570	0.1 %
Shrinkage rate	3.18mm，Flow	ASTM D955	1.7 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	28.3 MPa
Elongation at Break		ASTM D638	50 %
tensile strength	Yield	ASTM D-638	28.3 MPa
elongation	Break	ASTM D-638	50 %
Bending modulus		ASTM D-790	1380 MPa
bending strength		ASTM D-790	33.8 MPa
Bending modulus		ASTM D790	1380 MPa
bending strength		ASTM D790	33.8 MPa
Impact strength of cantilever beam gap	3.18mm	ASTM D256	267 J/m
Rockwell hardness		ASTM D785	78

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed		54.4 °C
Linear coefficient of thermal expansion	Flow	ASTM D-696	流动 cm/cm/°C
Hot deformation temperature	0.45MPa，Unannealed	ASTM D648	91.6 ℃
Hot deformation temperature	Hot deformation temperature	1.8MPa，Unannealed	ASTM D648	54.4 ℃
Linear coefficient of thermal expansion		ASTM D696	0.000072 cm/cm/℃
UL flame retardant rating	1.50mm	UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D-792	1.06 g/cm³
Shrinkage rate	MD 3.18 mm	ASTM D-955	1.7 %
Water absorption rate	24 hr	ASTM D-570	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D-257	10 到 1.0E+3 ohms
Volume resistivity		ASTM D-257	1.0 to 10 ohm·cm
Volume resistivity	Volume resistivity		ASTM D257	1-10 ohm·cm
Surface resistivity		ASTM D257	10-1E+3 ohms

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R -Sale	ASTM D-785	78

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.