Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| saturation | | % | 9.0 |
| Apparent density | | g/cm³ | 0.70-0.78 |
| viscosity number | | cm³/g | 138to247 |
| balance | | % | 2.5 |
| melt mass-flow rate | | g/10min | 1.2-5.0 |
| flow | | mm/mm | 152.4E-3-0.635 |
| saturation | | % | 7,9到11 |
| balance | | % | 2.5-3.5 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | | 45.03to201.38 Mpa |
| Shore hardness | | | 77to80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | % | 21to28 |
| Burning wire flammability index | | °C | 954to960 |
| Hot filament ignition temperature | | °C | 743to960 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | | 40.0to171.72 Mpa |
| fracture | | % | 3,0到77 |
| yield | | | 39.03to89.66 Mpa |
| fracture | | | 79.31to84.83 Mpa |
| fracture | | % | 2,2到12 |
| coefficient of friction | | | 0.30-1.0 |
| Nominal tensile fracture strain | | % | 5,6到50 |
| Tensile modulus | | | 477.24到0.01,0.04E0.05 Mpa |
| yield | | % | 3,0到21 |
| yield | | | 64.76to85.52 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 0.556to4.643 |
| Impact strength of simply supported beam without notch | | kJ/m² | 10.679to23.215 |
| Impact strength of cantilever beam gap | | kJ/m² | 1.988to6.176 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | 1.0E+2-2.5E+13 |
| Dissipation Factor | | | 0.020-0.30 |
| Volume resistivity | | | 3.50 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 87to202 |
| flow | | mm/mm/°C | 96.5E-5-152.4E-5 |
| horizontal | | mm/mm/°C | 99.1E-5-203.2E-5 |
| vicat | | °C | 67to247 |
| flow | | mm/mm/°C | 99.1E-5-101.6E-5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.