| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.25 g/cm³ |
| Shrinkage rate | | | 1.3to2.4 % |
| water content | | ISO 62 | 0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO 2039-2 | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ISO 527-2 | 38.0 MPa |
| Tensile strain | Break | ISO 527-2 | 30 % |
| Flexural modulus | | ISO 178 | 1500 MPa |
| bending strength | | ISO 178 | 55.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 1E+13 ohms |
| dielectric strength | | ASTM D149 | 15 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 120 °C |
| Heat distortion temperature | | ISO 75-2/A | 50.0 °C |
| melting temperature | | DSC | 220to225 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.3E-4到1.6E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.