Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 10 g/10min |
| Environmental stress cracking resistance | | ASTM D1693B | >1000 hr |
| density | | ASTM D1505 | 0.952 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 0.10 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 63 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Temperature | | | 210to230 °C |
| Blow molding temperature | | | 190to220 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTM D638 | 27.5 MPa |
| tensile strength | Break | ASTM D638 | 39.2 MPa |
| elongation | Break | ASTM D638 | 900 % |
| Flexural modulus | | ASTM D747 | 834 MPa |
| Flexural modulus | | ASTM D790 | 1080 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 460 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D15253 | 126 °C |
| melting temperature | | ASTM D3418 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.