Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Melt volume flow rate | | ISO 1133 | 70.0 cm3/10min |
Shrinkage rate | | ISO 2577 | 1.0 - 1.2 % |
Shrinkage rate | | ISO 2577 | 0.50 - 0.70 % |
Water absorption rate | | ISO 62 | 2.6 % |
flammability | Test Condition | Test Method | Test Result |
---|
burning rate | | FMVSS 302 | < 100 mm/min |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2/1 | 5200 Mpa |
tensile strength | | ISO 527-2/5 | 105 Mpa |
Tensile strain | | ISO 527-2/5 | 4.0 % |
Flexural modulus | | ISO 178 | 4900 Mpa |
bending strength | | ISO 178 | 190 Mpa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of simply supported beam without notch | | ISO 179/1eU | 45 kJ/m² |
Impact strength of simply supported beam without notch | | ISO 179/1eU | 70 kJ/m² |
injection | Test Condition | Test Method | Test Result |
---|
drying temperature | | | 75 to 85 °C |
drying time | | | 2.0 to 4.0 hr |
Processing (melt) temperature | | | 250 to 290 °C |
Temperature | | | 80 to 100 °C |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Hot deformation temperature (HDT) | | ISO 75-2/B | 215 °C |
Hot deformation temperature (HDT) | | ISO 75-2/A | 200 °C |
vicat | | ISO 306/B50 | 205 °C |
melting temperature | | ISO 11357-3 | 221 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.