Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D471 | 1.23 g/cm³ |
density | | ISO 2781 | 1.23 g/cm³ |
MeltViscosity | | ASTM D3835 | 740 Pa·s |
hardness | Test Condition | Test Method | Test Result |
---|
DurometerHardness | | ASTM D2240 | 72 |
Shore hardness | | ISO 868 | 72 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Taber abraser | | ASTM D1044 | 7.00 mg |
Torsion Module | | ASTM D1043 | 14.3 MPa |
Torsion Module | | ASTM D1043 | 2.20 MPa |
elastomer | Test Condition | Test Method | Test Result |
---|
compression set | | ASTM D395B | 55 % |
compression set | | ISO 815 | 15 % |
compression set | | ISO 815 | 55 % |
Clash Mountain Module | | ASTM D1043 | 68.9 MPa |
tensile strength | | ISO 37 | 12.4 MPa |
tensile strength | | ISO 188 | 13.1 MPa |
elongation | | ASTM D573 | 240 % |
elongation | | ASTM D412 | 270 % |
elongation | | ISO 37 | 270 % |
compression set | | ASTM D395B | 15 % |
Stretch permanent deformation | | ASTM D412 | 10 % |
tensile strength | | ASTM D412 | 5.30 MPa |
tensile strength | | ASTM D573 | 5.30 MPa |
tensile strength | | ISO 37 | 5.30 MPa |
tensile strength | | ISO 188 | 5.30 MPa |
tensile strength | | ASTM D412 | 12.4 MPa |
tensile strength | | ASTM D573 | 13.1 MPa |
elongation | | ISO 188 | 240 % |
tear strength | | ASTM D624 | 28.0 kN/m |
aging | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ISO 188 | -2.0 |
volume change | | ASTM D471 | 30 % |
volume change | | ASTM D471 | -9.0 % |
volume change | | ASTM D471 | 25 % |
volume change | | ASTM D471 | 8.0 % |
volume change | | ISO 1817 | 30 % |
volume change | | ISO 1817 | -9.0 % |
volume change | | ISO 1817 | 25 % |
volume change | | ISO 1817 | 8.0 % |
Hardness change rate in the air | | ASTM D573 | -2.0 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
brittle temperature | | ASTM D746 | -53.0 °C |
brittle temperature | | ISO 812 | -53.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.