Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.48 g/cm³ |
| Shrinkage rate | | | 0.40to0.80 % |
| Water absorption rate | | ASTM D570 | 0.20 % |
| density | | ASTM D792 | 1.48 |
| Water absorption rate | | ASTM D570 | 0.2 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 125 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 221 MPa |
| elongation | Break | ASTM D638 | 2.6 % |
| Flexural modulus | | ASTM D790 | 11800 MPa |
| Flexural modulus | | ASTM D790 | 120000 kgf/cm2 |
| Impact strength of cantilever beam gap | | ASTM D256 | 11 kgf.cm/cm |
| Rockwell hardness | | ASTM D786 | 125 R |
| bending strength | | ASTM D790 | 294 MPa |
| tensile strength | | ASTM D638 | 2250 kgf/cm2 |
| elongation | | ASTM D638 | 2.6 % |
| tensile strength | | ASTM D790 | 3000 kgf/cm2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 110 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 10-16 Ω.mm |
| internal voltage | | ASTM D149 | 22 KV/mm |
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 22 kV/mm |
| arc resistance | | ASTM D495 | 140 sec |
| arc resistance | | ASTM D495 | 140 Sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 300 °C |
| Heat distortion temperature | | ASTM D648 | 285 °C |
| melting temperature | | DSC | 310 °C |
| melting temperature | | ℃ | 310 ℃ |
| Heat distortion temperature | | ASTM D648 | 300 ℃ |
| Heat distortion temperature | | ASTM D648 | 285 ℃ |
| UL flame retardant rating | | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.